可将硫化或热塑性橡胶等产品在应变条件下，暴露于含一定浓度臭氧的空气中和在规定温度且无光线直接影响的环境中，检测其耐臭氧龟裂、应力变化、延长率等性能及可靠性。
Ozone can expose vulcanized or thermoplastic rubber and other products to the air with ozone and in the environment with a specified temperature and without direct effect of light under strain conditions to test its such performance and reliability as resistance to ozone cracking, variation of stresses and elongation ratio.
ASTM D1149 ASTM D1171 ASTM D1325 ISO1431 GB7762 HG/T 2869 JIS K 6259
| 工作室尺寸（mm）Test Space Dimensions | 700*800*900（D*W*H）（mm） |
| 外形尺寸 Overall Dimensions | 1840*1240*1150（D*W*H）（mm） |
| 臭氧浓度 Ozone Concentration | 低浓度Low Concentration：25~500pphm / 高浓度High Concentration： 25~1000pphm |
| 臭氧精确度 Ozone Diviation | ≤±5.0％F.S |
| 温度范围 Temp. Range | S1：RT~+65℃ / S2：+15℃～+65℃ |
| 温度波动度 Temp. Fluctuation | ≤±0.5℃ |
| 温度均匀度 Temp. Uniformity | ≤2.0℃ |
| 湿度范围 Humidity Range | S1：45%±10% / S1：30%~95%RH（可控） |
| 气体流速 Air Flow Speed | 8mm~16mm/s |
| 样架旋转速度 Sample Frame Rotary Speed | 1r~5r/min，可调Adjustable |
| 动态拉伸延长率 Dynamic Tensile Elongation | 0~50%±2%，可调Adjustable |
| 动态拉伸频率 Dynamic Stretch Frequency | 0.5~1.0Hz（±0.025 Hz） |
| 样件夹具 Sample Holder | 静态拉伸装置 / 动态拉伸装置 Static / Dynamic |
| 额定电压 Nominal Voltage | AC380V or 220V ±10%，50Hz |
| 功率 Power | 5.0(kW) |
| 重量 Weight | 320(kg) |
备注
1.设备性能在环境温度+25℃，相对湿度65%RH下，无负载所测。The performance vulues refer to environmental +25℃ 65%RH,no loading.
2.外形尺寸未包含局部突出部分。The ledge is not included in the overall dimensions.
生产及研发基地
地址：江苏省无锡市江阴市祝塘镇文林人民路152号
TEL：(+86)510-86086217 / 86086317
FAX：(+86)510-86082117
POST：214416
E-MAIL：sales@wxaswt.com
HTTP：//www.wxaswt.com-
Singapore Office （ATC Group）
ADD：24A Woodlands Loop Singapore 737891
Tel：+65 6362 1200
-
上海办事处
地址：上海市闵行区宜山路2000号利丰广场2号楼7楼
Tel：17321268655 -
深圳办事处
地址：深圳市南山区桂湾三路龙海家园21栋1004
Tel：13590219808
-
天津办事处
地址：天津市河西区黑牛城道顺驰世纪城17-3-1001（1101）
Tel：022-88295877